High Fluorine Content 68% FKM B Type Terpolymer Uncured FKM Compound Fluoroelastomer
Description:
Fluorine rubber: it has high chemical stability and has the best medium resistance in current all elastomers, the high temperature resistance is like silicone rubber, and is the best in current elastomers. Under high temperature condition, fluorine rubber has excellent oil resistance and can resist various chemical solvents and medium, so it is widely used in aerospace, military and various industries.
Through molding and extrusion, etc, to produce a variety of seals, O-rings, diaphragm, slab rubber and rubber strip, etc.
Fluoroelastomer terpolymer is called as FKM B by Dupon company, The higher the fluorine content of the fluorine rubber, the better the corrosion resistance, but at the same time the low temperature flexibility decreases.
It is composed of three monomers:VDF+TFE+HFP.It is widely used in corrosive automotive fuel systems, aircraft and chemical processing environments.
| FKM® | Fluorine Content% | Chemical resistance | Heat Resistance | Low temperature resistance | Compression set | Alkali Resistance |
| A | 66 | ++ | +++ | + | +++ | - |
| B | 68.5 | +++ | +++ | 0 | +++ | - |
Material data sheet:
H2801
| PROPERTY TEST REPORT | Report No: | S209 | ||||||
| Customer: | / | Test Date | 7.14 | |||||
| Product: | QFFB-H2801 | Material: | FKM | |||||
| Expiration date : | 180 days | Formulation No: | ||||||
| Our Ref: | 20071002 | Colour: | Black | |||||
| Press Cure | 170℃*10min | Post Cure: | 230℃*24h | |||||
| Room Temperature/ | 23℃ | Humidity: | 55% | |||||
| Test Item | Test Result | Test Method | ||||||
| Curing items : Test temperature :177℃ Test time:600 Sec | ||||||||
| (TS2)Scorch time,Ts2,sec | 1::4 | ASTM D1646 | ||||||
| (TC10)Scorch to10% cure,t'10,sec | 1::34 | ASTM D1646 | ||||||
| (TC90)Time to 90%cure,t'90,sec | 4:19 | ASTM D1646 | ||||||
| (ML)Minimum torque,ML,lbf-in | 2.69 | ASTM D1646 | ||||||
| (MH)Minimum torque,MH,dN-m | 19.33 | ASTM D1646 | ||||||
| Typical Properties Test: | ||||||||
| Hardness Shore A | 84 | ASTM D2240 | ||||||
| Tensile strength(MPa) | 11.9 | ASTM D412,Die C | ||||||
| Elongation(%) | 168 | ASTM D412,Die C | ||||||
| Remarks: | This is to certify that the above designated material has been tested and did comply with our Q.C.specifications. | |||||||
| Total judgement Passed | Mr. Zhang | Tester: | Ms. Chen | |||||
H27011
| PROPERTY TEST REPORT | Report No: | S209 | ||||||
| Customer: | / | Test Date | 7.2 | |||||
| Product: | QFFB-H2701 | Material: | FKM | |||||
| Expiration date : | 180 days | Formulation No: | ||||||
| Our Ref: | 20070203Y | Colour: | Black | |||||
| Press Cure | 170℃*10min | Post Cure: | 230℃*24h | |||||
| Room Temperature/ | 23℃ | Humidity: | 55% | |||||
| Test Item | Test Result | Test Method | ||||||
| Curing items : Test temperature :177℃ Test time:600 Sec | ||||||||
| (TS2)Scorch time,Ts2,sec | 1:02 | ASTM D1646 | ||||||
| (TC10)Scorch to10% cure,t'10,sec | 0:54 | ASTM D1646 | ||||||
| (TC90)Time to 90%cure,t'90,sec | 4:32 | ASTM D1646 | ||||||
| (ML)Minimum torque,ML,lbf-in | 2.39 | ASTM D1646 | ||||||
| (MH)Minimum torque,MH,dN-m | 16.30 | ASTM D1646 | ||||||
| Typical Properties Test: | ||||||||
| Hardness Shore A | 73 | ASTM D2240 | ||||||
| Tensile strength(MPa) | 13.8 | ASTM D412,Die C | ||||||
| Elongation(%) | 241 | ASTM D412,Die C | ||||||
| Remarks: | This is to certify that the above designated material has been tested and did comply with our Q.C.specifications. | |||||||
| Total judgement Passed | Mr. Zhang | Tester: | Ms. Chen | |||||
Picture shows: